PVDF 苏威41308 强度低分之量 聚偏二氟乙 烯 正涛 塑
Solef® 41308
Polyvinylidene Fluoride
Solvay Specialty Polymers
产品说明：
Solef® 41308/0001 PVDF专用于共挤。
物性信息：
| 加工方法 |
|
| 密度 | 1.78 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） | ASTM D1238 | ||
| 230°C/2.16 kg | 6.0 到 8.0 | g/10 min | ASTM D1238 |
| 230°C/5.0 kg | 18 到 24 | g/10 min | ASTM D1238 |
| 吸水率 1(23°C, 24 hr) | < 0.040 | % | ISO 62 |
| 拉伸模量 2(23°C) | 1900 | MPa | ASTM D638 |
| 抗张强度 3 | ASTM D638 | ||
| 屈服, 23°C | 48.0 | MPa | ASTM D638 |
| 断裂, 23°C | 30.0 | MPa | ASTM D638 |
| 伸长率 4(屈服, 23°C) | 7.0 | % | ASTM D638 |
| 摩擦系数 | ASTM D1894 | ||
| 与自身 - 动态 | 0.31 | ASTM D1894 | |
| 与自身 - 静态 | 0.32 | ASTM D1894 | |
| 泰伯耐磨性 (1000 Cycles, 1000 g, CS-10 转轮) | 8.00 | mg | ISO 5470-1 |
| 简支梁缺口冲击强度 5(23°C) | 8.5 | kJ/m² | ASTM D256 |
| 熔融温度 | 169 | °C | ASTM D3418 |
| 结晶峰温度 (DSC) | 136 | °C | ASTM D3418 |
| 结晶热 | 51.6 | J/g | ASTM D3418 |
| 融合热量 6 | 52.7 | J/g | ASTM D3418 |
| 表面电阻率 | > 1.0E+14 | ohms | ASTM D257 |
| 体积电阻率 | > 1.0E+14 | ohms·cm | ASTM D257 |
| 1 . | 方法1 |
| 2 . | 1.0 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 4mm厚，2m/s |
| 6 . | 80°C到熔融末端 |
PVDF材料参数：
外观，白色粉末 /气味 / 无 /
纯度，≥ % 99.5 PVDF
分散细度，≤ µm 35
刮板细度计 熔融指数 g/10min 0.5-2.0 D1238，230℃，
10kg 标准相对密度 g/cm3 1.75-1.77 D792，@23/23℃
熔点℃ 156-165 D341
热分解温度，≥ 390 TGA,1%Wt.Loss，Air
溶解性 / 澄清透明，无杂质 30℃，1hr 1g/10ml
含水率，≤ % 0.10 Karl Fischer
玻璃化温度-39℃
脆化温度-62℃以下
结晶熔点约170℃